Dynamic Hardness Evolution in Metals from Impact Induced Gradient Dislocation Density

Authors:
Preprint
Publisher website
Google Scholar
Abstract
A clear understanding of the dynamic behavior of metals is critical for developing superior structural materials as well as for improving material processing techniques such as cold spray and shot peening. Using a high velocity (from 120 m/s to 700 m/s; strain rates >10^7 1/s) micro-projectile impact testing and quasistatic (strain rates: 10^-2 1/s) nanoindentation, we investigate the strain-rate-dependent mechanical behavior of single-crystal aluminum substrates with (001), (011), and (111) crystal orientations. For all three crystal orientations, the dynamic hardness initially increases with increasing impact velocity and reaches a plateau regime at hardness 5 times higher than that of at quasistatic indentations. Based on coefficient of restitution and post mortem transmission Kikuchi diffraction analyses, we show that distinct plastic deformation mechanisms with a gradient dislocation density evolution govern the dynamic behavior. We also discover a distinct deformation regime-stable plastic regime-that emerge beyond the deeply plastic regime with unique strain rate insensitive microstructure evolution and dynamic hardness. Our work additionally demonstrates an effective approach to introduce strong spatial gradient in dislocation density in metals by high-velocity projectile impacts to enhance surface mechanical properties, as it can be employed in material processing techniques such as shot peening and surface mechanical attrition treatment.

This publication has 51 references indexed in Scilit: