On-Line Processing of Unidirectional Fiber Composites Using Radiative Heating: II. Radiative Properties, Experimental Validation and Process Parameter Selection

Authors:
Publisher website
Google Scholar
Abstract
Experimental validation is presented for a detailed thermal model (described in Paper I) for on-line processing of unidirectional fiber composites by surface or volumetric radiative heating. Surface and volumetric radiative properties of unidirectional graphite/epoxy and glass/epoxy are presented: measurements of the complex refractive index of an uncured and cured 3501-6 epoxy resin as a function of wavelength; semi-empirical extinction and scattering coefficients and phase functions for graphite/epoxy and glass/epoxy as a function of wavelength and incident angle, assuming independent scattering; model predictions of the effects of dependent scattering (i.e. electromagnetic wave interference) in graphite/epoxy and glass/epoxy; and measurements of the directional-hemispherical reflectance of AS4/3501-6 as a function of wavelength, incident angle, unidirectional composite orientation, and degree of cure. Experimental temperature histories for in-situ (or continuous) curing of graphite/epoxy, hoop-wound cylinders using infrared (IR) heating at power levels of 5 and 7 kW and mandrel winding speeds of 0.1 and 0.15 m/s are presented. Good qualitative agreement is found between the experimental results and model predictions for AS4/3501-6. Recommended manufacturing process windows for graphite/epoxy and glass/epoxy are presented for several process parameters, such as radiant-source emissive power level and winding speed. Due to their higher radiation absorptivity and lower heat capacity, graphite composites generally have narrower process windows.

This publication has 13 references indexed in Scilit: