Fatigue cracking from a corrosion pit in an aircraft bulkhead
Authors:
- S.A. BarterSBS.A. Barter
- L. MolentLML. Molent
- 1 April 2014
- journal article
- Published by Elsevier in Engineering Failure Analysis
- Vol. 39, 155-163
Abstract
No abstract availableKeywords
This publication has 7 references indexed in Scilit:
- Service fatigue cracking in an aircraft bulkhead exposed to a corrosive environmentEngineering Failure Analysis, 2013
- Exfoliation Corrosion and Pitting Corrosion and Their Role in Fatigue Predictive Modeling: State-of-the-Art ReviewInternational Journal of Aerospace Engineering, 2012
- The lead crack fatigue lifing frameworkInternational Journal of Fatigue, 2011
- Scientific advances enabling next generation management of corrosion induced fatigueProcedia Engineering, 2011
- Fatigue crack growth from flaws in combat aircraftInternational Journal of Fatigue, 2010
- Characterisation of equivalent initial flaw sizes in 7050 aluminium alloyFatigue & Fracture of Engineering Materials & Structures, 2006
- THE FATIGUE RESISTANCE OF PEENED 7050‐T7451 ALUMINIUM ALLOY—REPAIR AND RE‐TREATMENT OF A COMPONENT SURFACEFatigue & Fracture of Engineering Materials & Structures, 1994