Improvement of the Surface Layer Properties of 316L Stainless Steel Produced by DMLS Through the Use of a Shot Peening Process

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Additive-manufactured (AM) 316L stainless steel, produced via direct metal laser sintering (DMLS) and characterised by a surface topography of high irregularities and tensile residual stresses with specific anisotropy, was subjected to milling and shot peening. The milling process caused a reduction in surface topography parameters, but tensile residual stresses increased significantly. The shot peening process was carried out according to the full factorial design 32 and technological parameters such as a shot diameter in the range of 1-3 mm and an air supply pressure between 0.2 and 0.6 MPa. As a result of the experiments and the analysis, reduced surface topography was achieved, and a favourable residual stress state was formed with compressive stresses. The mechanism of the changes was demonstrated via microstructure observation and statistical models obtained by mathematical analysis.

This publication has 31 references indexed in Scilit: