Enhancing Lubrication Performance of Calcium Sulfonate Complex Grease Dispersed with Two-Dimensional MoS2 Nanosheets

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Calcium sulfonate complex greases (CSCG) have proven to be a sustainable alternative to lithium complex greases, which still require appropriate additives to deliver lubrication performance benefits under extreme working conditions such as heavy load, high speed, and high temperature. The anti-wear and friction reducing properties of CSCG enhanced by two-dimensional MoS2 nanosheets (2D MoS2) with a narrow lateral size and thickness distributions were evaluated by a four-ball tribometer. The results showed that the CSCG with 0.6 wt.% 2D MoS2 performs best, with a 56.4% decrease in average friction coefficient (AFC), 16.5% reduction in wear scar diameter (WSD), 14.3% decrease in surface roughness, and a 59.4% reduction in average wear depth. Combining SEM-EDS images, Raman, and X-ray photoelectron spectra, it is illustrated that the physical transferred film and tribo-chemical film consisting of MoS2, Fe2O3, FeSO4, CaCO3, CaO, and MoO3 were generated on the worn surface, which improves the lubrication performance of CSCG considerably.
Funding Information
  • Natural Science Foundation of Chongqing Municipality (cstc2019jcyj-msxmX0453, KJZD-K202212905)
  • Science and Technology Research Program of Chongqing Municipal Education Commission (cstc2019jcyj-msxmX0453, KJZD-K202212905)

This publication has 28 references indexed in Scilit: