Difference in Reheat Cracking Susceptibility of 2.25Cr-W and 9Cr-W Heat-resistant Steels
Authors:
Open Access
- 1 January 2017
- journal article
- Published by Iron and Steel Institute of Japan in ISIJ International
- Vol. 57 (7) , 1268-1272
Abstract
This research has been performed to evaluate the reheat cracking susceptibility of 9Cr T/P92 heat-resistant steels and find the difference in susceptibility between 2.25Cr T/P23 and 9Cr T/P92 heat-resistant steels. After the welding simulation at 1200°C and 1300°C, the prior austenite grain size is much smaller in the T/P92 steel than the T/P23 steel. This is attributed to the undissolved Nb-rich carbo-nitrides in the T/P92 during the welding simulation which inhibit the growth of prior austenite grains. After tensile test at 750°C for the evaluation of cracking susceptibility, the fracture mode is typically intergranular in the T/P23 steel, while that of the T/P92 is ductile. Therefore, the insensitivity to intergranular cracking of the T/P92 steel is mainly attributed to the much lower phosphorus segregation concentration at grain boundaries which is caused by the smaller prior austenite grain size. Calculation results finally confirm that the grain boundary segregation concentration of phosphorus decreases with decreasing grain size.Keywords
This publication has 22 references indexed in Scilit:
- Study on grain boundary character and strain distribution of intergranular cracking in the CGHAZ of T23 steelMaterials Characterization, 2013
- Creep-resistant steels2008
- New Generation 21/4Cr Steels T/P 23 and T/P 24 Weldability and High Temperature PropertiesWelding in the World, 2005
- Investigation of hydrogen attack in 2.25Cr1Mo steels with a high-triaxiality void growth modelActa Materialia, 1996
- Mechanisms of stress relief cracking in a ferritic steelActa Metallurgica, 1984
- A study of stress relief cracking in 1 Mo steel—I. The effects of P segregationActa Metallurgica, 1980
- Overview no. 2Acta Metallurgica, 1979
- Nucleation of cavities at second phase particles in grain boundariesActa Metallurgica, 1978
- Intergranular fracture at elevated temperatureActa Metallurgica, 1975
- The growth of grain-boundary voids under stressPhilosophical Magazine, 1959