Rare earth scandate thin films by atomic layer deposition: effect of the rare earth cation size
- 14 April 2010
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Journal of Materials Chemistry
- Vol. 20 (20) , 4207-4212
Abstract
A series of amorphous REScO3 films was deposited by atomic layer deposition (ALD) using rare earth (RE) β-diketonate precursors RE(thd)3 (thd = 2,2,6,6-tetramethyl-3,5-heptanedionato) together with ozone in an attempt to study the effect of the RE3+ cation size on various film properties. A clear correlation between the deposition rate and the RE3+ cation radius was established. REScO3 films with a metal ratio RE : Sc close to the stoichiometric one, viz. RE : Sc = 1, and a small excess of oxygen were realized by adjusting the metal precursor pulsing ratio. Small amount of carbon was found as impurity in all the films, concentrations varying from 1–3 at% (RE = La, Gd or Dy) to 0.4–0.5 at% (RE = Er or Lu). Also the crystallization temperature and the resulting phase were affected by the RE3+ cation size. The REScO3 films were found to crystallize either as an orthorhombic perovskite phase or as a solid solution of the cubic C-type oxides. High crystallization temperatures of 800–900 °C were observed for LaScO3, GdScO3 and DyScO3. All the films gave smooth C–V curves with very small hysteresis (typically κ ≈ 24) was found for DyScO3. Also the leakage current densities were small, typically in a range of 10−6–10−9 A cm−2 at 1 V. The results confirm that REScO3 films deposited by ALD are potential candidates for new generation high-κ gate dielectrics.Keywords
This publication has 30 references indexed in Scilit:
- Investigation of terbium scandate as an alternative gate dielectric in fully depleted transistorsApplied Physics Letters, 2010
- Thin films of high-k dysprosium scandate prepared by metal organic chemical vapor deposition for metal–insulator–metal capacitor applicationsSolid State Communications, 2008
- SmScO 3 thin films as an alternative gate dielectricApplied Physics Letters, 2008
- Characterization and electrical properties of high-k GdScO3 thin films grown by atomic layer depositionApplied Physics A, 2007
- Dysprosium scandate thin films as an alternate amorphous gate oxide prepared by metal-organic chemical vapor depositionApplied Physics Letters, 2006
- Gadolinium scandate thin films as an alternative gate dielectric prepared by electron beam evaporationApplied Physics Letters, 2006
- Preparation and characterization of rare earth scandates as alternative gate oxide materialsSolid-State Electronics, 2006
- Metallorganic Chemical Vapor Deposition of Dysprosium Scandate High-k Layers Using mmp-Type PrecursorsJournal of the Electrochemical Society, 2006
- Ternary rare-earth metal oxide high-k layers on silicon oxideApplied Physics Letters, 2005
- High-κ gate dielectrics: Current status and materials properties considerationsJournal of Applied Physics, 2001