Preparation and characterization of poly(methyl methacrylate)–lead silicate composites

Authors:
Publisher website
Google Scholar
Abstract
Poly(methyl methacrylate)–lead silicate composites were prepared with different amounts of crystalline or amorphous PbO–SiO2 binary composition (70 mole % PbO). The polymerization reaction was carried out in aqueous medium and in methanol–water mixture at 40°C using sodium bisulfite as initiator. The presence of lead silicate was found to increase the molecular weight of the poly(methyl methacrylate). The prepared composites were characterized by studying their shielding properties to γ radiation, mechanical hardness, dielectric constant, and thermal stability. It was found that lead silicate increases the absorbing power of the composites to γ radiation. This behavior was found to be dependent on the amount and the type of lead silicate (amorphous or crystalline). Gamma irradiation of the composites was found to cause chemical degradation of the poly(methyl methacrylate) leading to a decrease in mechanical hardness. Molecular weights of the poly(methyl methacrylate) for some of the composites were determined before and after irradiation viscosimetrically. Dielectric constants for some of the composites were determined at two different temperatures. The thermal stability of the composites was studied by means of an automatic thermogravimetric analyzer.

This publication has 3 references indexed in Scilit: