Unveiling robust spin-phonon coupling and magnetic-order-driven phonon softening in honeycomb Mn 3 NiTa 2 O 9

Authors:
Publisher website
Google Scholar
Abstract
Observation and interpretation of the temperature dependence of the prominent Raman modes of Mn 3 NiTa 2 O 9 (MNTO) from T = 8 to 300 K is reported and compared with those reported in the isostructural Mn 4 Ta 2 O 9 (MTO) with honeycomb lattice and trigonal symmetry. The systematic blue shift of all Raman modes of MNTO relative to those in MTO is interpreted to result from the reduced lattice parameters of MNTO due to Ni substitution. The smaller magnetic moment of Ni 2 + relative to that of Mn 2 + is the likely source of a few % reduction in the observed magnetic transitions ( T N ∼ 97 K and T S ∼ 46 K) of MNTO. The phonon frequencies ( ω ) and linewidths ( Γ ) were obtained by fitting each Raman mode with a single Lorentzian profile. For T > T N , the phonon frequencies decrease monotonically while the linewidths broaden with increasing temperatures, these results are well described by a three-phonon anharmonic decay model. With decreasing temperatures below T N , pronounced softening of nearly all Raman modes in MNTO is observed, becoming particularly significant below T S in contrast to MTO, where phonon hardening was reported. These anomalous phonon shifts are attributed to strong spin-phonon coupling ( λ ), which is positive in MNTO but negative in MTO. The reversal in the sign of λ in MNTO highlights a fundamental modification of the spin-lattice interaction induced by Ni substitution demonstrating that subtle structural changes can profoundly alter the coupling between lattice vibrations and magnetic order in the honeycomb magnetoelectric tantalates.
Funding Information
  • ANR (ANR-23-EXES-0001)
  • DST SERB (CRG/2022/006155)
  • Université of Caen
  • Ministry of Science and Technology, Government of India
  • Council of Scientific and Industrial Research
  • French Government
  • Normandy Region
  • UGC-DAE CSR (CRS/202122/01/383)
  • Ministry of Education, India

This publication has 26 references indexed in Scilit: