Titanium coordination in silicate glasses investigated using O K-edge X-ray absorption spectroscopy

Authors:
  • GHG. S. Henderson
    G. S. Henderson
  • XLXiaoyang Liu
    Xiaoyang Liu
  • MFM. E. Fleet
    M. E. Fleet
Publisher website
Google Scholar
Abstract
A series of titanium silicate glasses along the composition joins TiO2-SiO2, TiO2-Na2SiO3, TiO2-K2SiO3 and TiO2-CaSiO3, has been examined using oxygen K-edge X-ray absorption near edge structure spectroscopy (XANES) confined to the near-surface region. Sharp pre-edge features in the spectra can be used to determine the Ti coordination in the glasses. The presence of [4]Ti is indicated by a pre-edge peak at ∼534 eV while [5]Ti is indicated by a peak at ∼533 eV. Titanium exists in all these glasses as [4]Ti and [5]Ti with no [6]Ti being present. For alkali-containing glasses the [5]Ti site becomes more prevalent with increasing TiO2. TiO2-K2SiO3 compositions contain a greater proportion of [4]Ti than comparable Na2O compositions. This is consistent with earlier Ti L-edge findings. The TEY spectra for the TiO2-CaSiO3 compositions indicate the presence of significant amounts of [5]Ti at high TiO2 contents; however, comparison of TEY (near surface) and FY (bulk sample) XANES shows that the [5]Ti is confined to the surface of the glass sample with the bulk of the glass containing [4]Ti.

This publication has 15 references indexed in Scilit: