Improvement in the photoelectrochemical water-splitting performance using GaN nanowires with bundle structures
- 12 August 2021
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Journal of Materials Chemistry C
- Vol. 9 (37) , 12802-12810
Abstract
We report an approach for improving the photoelectrochemical water splitting (PEC–WS) performance using GaN-nanowire (NW) bundles (GNW-BDLs) as the photoanode material. The bundles were formed by dipping GaN NWs with an average length of 648.3 nm and diameter of 35.2 nm into acetone. The effect thereof was that the upper sections of several NWs were agglomerated via van der Waals bonding to form a bundle structure. The current density and applied bias photon-to-current efficiency of the GNW-BDL photoanode in a 0.5 M H2SO4 electrolyte were measured to be 2.2 mA cm−2 and 1.9%, respectively, at 0.6 V vs. reversible hydrogen electrode. These values were increased by 314% and 317% compared with those (0.7 mA cm−2 and 0.6%) of the photoanode using pristine GaN NWs. In addition, the PEC–WS performance was observed at the potential of 0 V vs. Pt. This remarkable improvement is largely attributed to the reduction in the effect of the surface-trap states of GaN NWs on the migration of the photogenerated carriers to the electrolyte because of the formation of structures consisting of bundles of neighboring NWs.Keywords
Funding Information
- Ministry of Education (2018R1D1A1B07043442)
This publication has 73 references indexed in Scilit:
- High efficiency photoelectrochemical water splitting and hydrogen generation using GaN nanowire photoelectrodeNanotechnology, 2013
- Impact of native defects in high‐k dielectric oxides on GaN/oxide metal–oxide–semiconductor devicesPhysica Status Solidi (b), 2013
- 3D branched nanowire heterojunction photoelectrodes for high-efficiency solar water splitting and H2 generationNanoscale, 2012
- Macro- and micro-strain in GaN nanowires on Si(111)Nanotechnology, 2011
- Wafer-Level Photocatalytic Water Splitting on GaN Nanowire Arrays Grown by Molecular Beam EpitaxyNano Letters, 2011
- X-ray analysis of ZnO nanoparticles by Williamson–Hall and size–strain plot methodsSolid State Sciences, 2011
- Steady-state and transient photoconductivity in c-axis GaN nanowires grown by nitrogen-plasma-assisted molecular beam epitaxyJournal of Applied Physics, 2010
- Underwater adhesion of abalone: The role of van der Waals and capillary forcesActa Materialia, 2009
- Nanohomojunction (GaN) and Nanoheterojunction (InN) Nanorods on One‐Dimensional GaN Nanowire SubstratesAdvanced Functional Materials, 2004
- Turnstile device for heralded single photons: Coulomb blockade of electron and hole tunneling in quantum confinedp-i-nheterojunctionsPhysical Review Letters, 1994