Effects of transparent conducting electrodes and hole transport layers on the performance of MAPbI3 solar cells fabricated on PET substrates

Authors:
Open Access
Publisher website
Google Scholar
Abstract
This study investigates how the performance of perovskite solar cells (PSCs) made on polyethylene terephthalate (PET) substrates depends on transparent conducting electrodes (TCEs) and hole transport layers (HTLs). We fabricated PSCs using commercially available PET/TCEs and compared their performance with PSCs manufactured on Glass/indium tin oxide (ITO) substrates. Poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) with varying levels of acidity and NiO nanoparticles were used as HTLs. The current density-voltage characteristics of PSCs made on PET/TCEs were found to be significantly lower when highly acidic PEDOT:PSS was used as the HTL. However, this was not observed for PSCs made on Glass/ITO. To investigate the interaction between HTL and TCE, atomic force microscopy was carried out after dipping the TCEs in PEDOT:PSS solutions of different acidity. X-ray photoelectron spectroscopy measurements further revealed differences in the chemical composition between ITO film on PET vs. on glass. Our results indicate that the performance of PSCs depends both on the TCE substrates and HTLs, which can be explained by their chemical interaction.
Funding Information
  • Solar Energy Technologies Office (DE-EE0009518)
  • The University of Texas at Dallas (Texas Instruments Distinguished Chair in Nanoelectronics)

This publication has 31 references indexed in Scilit: