Synthesis and property of polyoxazolidone having fluorene moiety by polyaddition of diisocyanate and diepoxide

Authors:
Publisher website
Google Scholar
Abstract
Polyoxazolidones having fluorenyl group were synthesized by polyaddition of 9,9‐diglycidyl fluorene with various diisocyanates. The polymer from 9,9‐diglycidyl fluorene and methylenediphenyl 4,4′‐diisocyanate was afforded in high yield although polydispersity of the polymer was found relatively broad. The IR spectrum of the obtained polymer showed two absorption in carbonyl region. One of them was assigned to the expected oxazolidone, while the other at 1710 cm−1 appeared due to a carbonyl group of the isocyanurate moieties produced by cyclotrimerization of isocyanate. It is assumed that the cyclotrimerization would cause the broad polydispersity caused by the branched structure formed by isocyanurate. The polymers obtained with three kinds of diisocyanates (methylenediphenyl 4,4'‐diisocyanate, 1,6‐hexamethylene diisocyanate, 1,4‐phenylene diisocyanate) showed high thermal stability, as their Td10 was depended on the structure of diisocyanate. All polymers had high transparency in a visible region. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014, 52, 1755–1760

This publication has 17 references indexed in Scilit: