Thermodynamic Modeling and Validation of the Temperature Influence in Ternary Phase Polymer Systems

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The effect of the temperature, as a process variable in the fabrication of polymeric membranes by the non-solvent induced phase separation (NIPS) technique, has been scarcely studied. In the present work, we studied the influence of temperature, working at 293, 313 and 333 K, on the experimental binodal curves of four ternary systems composed of PVDF and PES as the polymers, DMAc and NMP as the solvents and water as the non-solvent. The increase of the temperature caused an increase on the solubility gap of the ternary system, as expected. The shift of the binodal curve with the temperature was more evident in PVDF systems than in PES systems indicating the influence of the rubbery or glassy state of the polymer on the thermodynamics of phase separation. As a novelty, the present work has introduced the temperature influence on the Flory–Huggins model to fit the experimental cloud points. Binary interaction parameters were calculated as a function of the temperature: (i) non-solvent/solvent (g12) expressions with UNIFAC-Dortmund methodology and (ii) non-solvent/polymer (χ13) and solvent/polymer (χ23) using Hansen solubility parameters. Additionally, the effect of the ternary interaction term was not negligible in the model. Estimated ternary interaction parameters (χ123) presented a linear relation with temperature and negative values, indicating that the solubility of the polymers in mixtures of solvent/non-solvent was higher than expected for single binary interaction. Finally, PES ternary systems exhibited higher influence of the ternary interaction parameter than PVDF systems.
Funding Information
  • Ministerio de Asuntos Económicos y Transformación Digital, Gobierno de España (CTM2016-75509-R)
  • Agencia Estatal de Investigación (PCI2018-092929, PID2019-105827RB-I00/AEI/10.13039/501100011033)

This publication has 52 references indexed in Scilit: