Novel Cyclosilazane-Type Silicon Precursor and Two-Step Plasma for Plasma-Enhanced Atomic Layer Deposition of Silicon Nitride

Authors:
Publisher website
Google Scholar
Abstract
We designed cyclosilazane-type silicon precursors and proposed a three-step plasma-enhanced atomic layer deposition (PEALD) process to prepare silicon nitride films with high quality and excellent step coverage. The cyclosilazane-type precursor, 1,3-di-isopropylamino-2,4-dimethylcyclosilazane (CSN-2) has a closed ring structure for good thermal stabil-ity and high reactivity. CSN-2 showed thermal stability up to 450°C and a sufficient vapor pressure of 4 Torr at 60°C. The energy for the chemisorption of CSN-2 on the undercoordinated silicon nitride surface was calculated to be -7.38 eV by density functional theory method. The PEALD process window was between 200 and 500°C with a growth rate of 0.43 Å/cycle. The best film quality was obtained at 500°C with hydrogen impurity of ~7 at.%, oxygen impurity less than 2 at.% and low wet etching rate and excellent step coverage of ~95%. At 300°C and lower temperatures, the wet etching rate was high especially at the lower sidewall of the trench pattern. We introduced the three-step PEALD process to improve the film quality and the step coverage on the lower sidewall. The sequence of the three-step PEALD process consists of the CSN-2 feeding step, the NH3/N2 plasma step, and the N2 plasma step. The H radicals in NH3/N2 plasma efficiently remove the ligands from the precursor, and the N2 plasma after the NH3 plasma removes the surface hydrogen atoms to activate the adsorption of the precursor. The films deposited at 300°C using the novel precursor and the three-step PEALD process showed a significantly improved step coverage of ~95% and excellent wet etching re-sistance at the lower sidewall, which is only twice as high as the blanket film prepared by low-pressure chemical vapor deposition (LPCVD).
Funding Information
  • Korea Evaluation Institute of Industrial Technology (10041792)

This publication has 32 references indexed in Scilit: