Effect of micro-cracking on the thermal conductivity and thermal expansion of tialite (Al2TiO5) ceramics

Authors:
  • RPRamanathan Papitha
    Ramanathan Papitha
  • MSMadireddy Suresh
    Madireddy Suresh
  • DDDibakar Das
    Dibakar Das
  • RJRoy Johnson
    Roy Johnson
Open Access
Publisher website
Google Scholar
Abstract
The pure and magnesium silicate (Mg2+/Si4+) doped tialite ceramics were prepared from the homogenized mixture of alumina and titania by uniaxial pressing and pressure-less sintering at 1550 °C in air. Thermal conductivity and thermal expansion of the doped and undoped tialite ceramics were measured from 30 to 700 \ud °C. The identical trend in the behaviour of these thermal properties most probably is influenced by the population, size and shape of microcracks present throughout the grain and grain boundaries as complemented by the microstructural observations. The observed decrease in thermal properties of the doped in comparison to \ud the pure tialite can be attributed to the substitutional Mg2+ and Si4+ at Al3+ site in Al2TiO5 which promotes the phonon scattering and causes modifications in micro-crack density and the morphology of the cracks