Effect of Heat Treatment on Grain Size, Phase Assemblage, and Mechanical Properties of 3 mol% Y‐TZP

Authors:
Publisher website
Google Scholar
Abstract
The effect of heat treatment on the grain size, phase assemblage, and mechanical properties of a 3 mol% Y‐TZP ceramic was investigated. Specimens were initially sintered for 2 h at 1450°C to near theoretical density; some specimens were then heat‐treated at 1550°, 1650°, 1750°, or 1850°C to coarsen the microstructure. The average grain size increased with heat treatment from 1750°C. The maximum fraction of tetragonal phase that transformed during fracture corresponded with the largest tetragonal grain size of ∼5–6 μm. Strength was on the order of 1 GPa, and was surprisingly insensitive to heat‐treatment temperature and grain size, contrary to previous studies. The fracture toughness increased from 4 to 10 MPa.m1/2 with increasing grain size, owing to an increasing transformation zone size. Grain sizes larger than 5–6 μm spontaneously transformed to monoclinic phase during cooling. Such critical grain sizes are much larger than those found in past investigations, and may be due to the greater fraction of cubic phase present which decreases the strain energy arising from crystallographic thermal expansion anisotropy of the tetragonal phase.

This publication has 26 references indexed in Scilit: