Preparation of superhydrophobic conductive micro/nano‐graphite/PDMS films on paper by simple spraying method

Authors:
Publisher website
Google Scholar
Abstract
Paper‐based materials are widely used in various fields due to their advantages, such as environmental friendliness and sustainability. However, the highly hydrophilic nature of the cellulose that makes up paper‐based materials limits their use. In this paper, micron/nano‐graphite/polydimethylsiloxane (PDMS) coatings with excellent superhydrophobic and conductive properties were prepared on the surface of filter paper by a simple spraying method. A mixture of micro‐graphite and nano‐graphite was used to form a multistage rough structure on the surface of the filter paper by spraying, and the low surface energy PDMS enhanced the adhesion of the micro‐graphite and nano‐graphite on the surface of the filter paper. The results showed that the samples possessed the best superhydrophobic properties when the ratio of micro‐graphite to nano‐graphite was 1:1, at which time the contact and rolling angles of the samples were 165.4° and 3.2°, respectively. The prepared superhydrophobic samples have good bounce and self‐cleaning properties, while the samples have good mechanical stability and chemical resistance. Additionally, due to the conductivity of micro–nano‐graphite, both particle sizes closely contact the sample surface, creating a conductive network. With a 1:1 ratio of micro‐ and nano‐graphite, the coating exhibits minimal resistance at 1.89 KΩ, and the sample maintains stable conductivity even underwater. The above properties greatly extend the application range of paper‐based superhydrophobic materials.
Funding Information
  • Key Laboratory of Icing and Anti/De-icing of Aircraft (IADL20220406)
  • Special Funds for the Basic Research and Development Program in the Central Non-profit Research Institutesof China (221111321000)

This publication has 31 references indexed in Scilit: