Gigacycle Fatigue Properties of Double-Melted SCM440 Steel and Size Effects
- 1 January 2014
- journal article
- research article
- Published by Iron and Steel Institute of Japan in ISIJ International
- Vol. 54 (6) , 1436-1442
Abstract
No abstract availableKeywords
This publication has 23 references indexed in Scilit:
- Influence of inclusion size on S‐N curve characteristics of high‐strength steels in the giga‐cycle fatigue regimeFatigue & Fracture of Engineering Materials & Structures, 2009
- Effect of test frequency on fatigue strength of low carbon steelFatigue & Fracture of Engineering Materials & Structures, 2009
- The effect of frequency on the giga‐cycle fatigue properties of a Ti–6Al–4V alloyFatigue & Fracture of Engineering Materials & Structures, 2008
- 1010‐cycle fatigue properties of 1800 MPa‐class JIS‐SUP7 spring steelFatigue & Fracture of Engineering Materials & Structures, 2003
- Fatigue crack propagation behaviour derived from S–N data in very high cycle regimeFatigue & Fracture of Engineering Materials & Structures, 2002
- High‐cycle rotating bending fatigue property in very long‐life regime of high‐strength steelsFatigue & Fracture of Engineering Materials & Structures, 2002
- Evaluation of giga‐cycle fatigue properties of some maraging steels by intermittent ultrasonic fatigue testingFatigue & Fracture of Engineering Materials & Structures, 2002
- Mechanism of fatigue failure in ultralong life regimeFatigue & Fracture of Engineering Materials & Structures, 2002
- S–N curve characteristics and subsurface crack initiation behaviour in ultra‐long life fatigue of a high carbon‐chromium bearing steelFatigue & Fracture of Engineering Materials & Structures, 2001
- Stepwise S‐N curve and fish‐eye failure in gigacycle fatigueFatigue & Fracture of Engineering Materials & Structures, 1999