Failure Study of Creep and High-Temperature Tensile Tested Tungsten Inert Gas Welded P92 Steel and AISI 304L Steel Dissimilar Weld Joints

This publication has 46 references indexed in Scilit:

• New insight on the solidification path of an alloy 625 weld overlay
  Journal of Materials Research and Technology, 2013
• Microstructures and mechanical properties of T92/Super304H dissimilar steel weld joints after high-temperature ageing
  Materials & Design (1980-2015), 2013
• High-temperature short-term tensile test and creep rupture strength prediction of the T92/TP347H dissimilar steel weld joints
  Engineering Failure Analysis, 2012
• Microstructure and creep characteristics of dissimilar T91/TP316H martensitic/austenitic welded joint with Ni-based weld metal
  Materials Characterization, 2012
• Microstructure and type IV cracking behavior of HAZ in P92 steel weldment
  Materials Science and Engineering: A, 2012
• Microstructural analysis on creep properties of dissimilar materials joints between T92 martensitic and HR3C austenitic steels
  Materials Science and Engineering: A, 2011
• Assessment of creep rupture properties for dissimilar steels welded joints between T92 and HR3C
  Fatigue & Fracture of Engineering Materials & Structures, 2011
• Characterization of high temperature deformation behavior of INCONEL 617
  Mechanics of Materials, 2009
• Failure analysis and remaining life assessment of service exposed primary reformer heater tubes
  Engineering Failure Analysis, 2008
• Transition metal joints for steam generators—An overview
  International Journal of Pressure Vessels and Piping, 1994