(E)‐1,2‐Bis(3,5‐dinitro‐1H‐pyrazol‐4‐yl)diazene – Its 3D Potassium Metal–Organic Framework and Organic Salts with Super‐Heat‐Resistant Properties

Authors:
Publisher website
Google Scholar
Abstract
(E)‐1,2‐Bis(3,5‐dinitro‐1H‐pyrazol‐4‐yl)diazene (H2NPA, 1) and its energetic salts, which are a series of new, energetic, highly heat‐resistant, dense explosives, were synthesized. The explosives contain four nitro groups and an azo‐bridged framework and were characterized by 1H and 13C NMR (in some cases 15N NMR) spectroscopy, IR spectroscopy, and elemental analysis. The crystal structures of K2NPA (a three‐dimensional metal–organic framework, 3D MOF) and the guanidinium salt 4 were determined by single‐crystal X‐ray diffraction, and their properties (density, thermal stability, and sensitivity towards impact and friction) were investigated. The detonation properties were evaluated from the measured density and calculated heat of formation by the EXPLO5 v6.01 program. All of the salts exhibit thermal stabilities with decomposition temperatures ranging from 156 to 315 °C, high densities (1.70–2.15 g cm–3), high detonation velocities (8224–9083 m s–1), and high positive heats of formation (45.7–1040.1 kJ mol–1). The obtained 3D metal–organic framework explosive K2NPA combines exceptional thermal stability (Td = 315 °C) with a high density (d = 2.15 g cm–3) and possesses ideal calculated detonation velocity (vD = 8275 m s–1) and pressure (PCJ = 31.1 GPa) values. Moreover, its suitable impact sensitivity (IS) of 1.5 J and friction sensitivity (FS) of 60 N make K2NPA an outstanding, highly heat‐resistant, green primary explosive. The guanidinium salt 4 also exhibits a high thermal stability (Td = 304 °C) that is superior to that of HMX, insensitivity to impact (IS > 40 J) and friction (FS > 360 N) comparable to those of 1,3,5‐triamino‐2,4,6‐trinitrobenzene (TATB), and a high detonation performance (vD = 8391 m s–1).
Funding Information
  • National Natural Science Fund Project (21672022)

This publication has 32 references indexed in Scilit: