Structure of glassy polymers. VII. Small‐angle X‐ray scattering from epoxy resins

Authors:
Publisher website
Google Scholar
Abstract
The small‐angle x‐ray scattering (SAXS) from an Epon 812 and two Epon 828 (one amine‐cured and one anhydride‐cured) epoxy resins has been measured using a Bonse‐Hart system. The data cover the angular range (2θ) between 20 sec and 60 min. After correction for absorption, background and vertical beam divergence, they have been placed on an absolute basis by comparison with the scattering from a previously studied polycarbonate sample. The corrected absolute intensity decreases strongly with increasing angle between 20 sec and 2 min, decreases more gradually between 2 and 20–30 min, and reaches a nearly constant asymptotic value at larger angles. The magnitude of the intensity in the constant‐intensity region is close to the value predicted by thermodynamic fluctuation theory for fluids applied at the glass transition temperature. The increase in intensity at angles smaller than 20–30 min is associated with heterogeneities in the cured resins. These heterogeneities cover a range of sizes in all samples, from less than 100 Å to more than 1000 Å, with the most frequently occurring size in the range 100–200 Å.

This publication has 18 references indexed in Scilit: