Manufacturing features, structure, and properties of high-purity Mo-Re thin sheets

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Manufacturing features, structure and properties of low-alloyed molybdenum sheets 0.5 mm thick made from the experimental Mo-3 wt.% Re single crystal are described and discussed in the present work. The developed technological scheme includes warm rolling of the initial ingot at a temperature of 1150 °C, with heating in the argon protective atmosphere, subsequent annealing at 850 °C for 2/3 h in a vacuum, no less than 1 ·103mmHg, cold rolling at a temperature of 400 °C, and post-deformation annealing at 800 C for 1/2 h. The results of micro structure analysis, physical and mechanical studies show that thin sheets are characterized by simultaneously high strength and plasticity, as well as the required temperature coefficient of linear expansion (TCLE), necessary for bonding with a glass by a thermo-compression welding. Obtained results reveal perspectives for the development of the application of thin Mo-3 wt.% Re sheets in vacuum engineering for the vacuum-tight metal-glass parts.