Influence of Rust Inhibitor on the Corrosion Resistance of Reinforcement in Cement Paste with Chloride

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The electrical resistance and polarization effect of cement paste containing reinforcement were tested to research the anti-corrosion properties of steel bars in cement paste. Moreover, the microstructure and composition of passivation film and rust on the steel bars were studied. The water–cement ratio of the cement paste in this study was 0.3, with 0.5% NaCl, 1% NaNO2, and 1% Benzotriazole, and an assembly unit of 0.5% NaNO2 + 0.5% Benzotriazole by mass of cement was added to the cement to provide a chloride environment. X-ray photoelectron spectroscopy (XPS) and scanning electron microscope (SEM) were applied to research the composition of the passivation film and the microstructure of the cement paste, respectively. The results indicated that the samples with the assembly unit of 0.5% NaNO2 + 0.5% Benzotriazole showed the highest electrical resistance and polarization electrical resistance, while the specimens with 1.0% Benzotriazole showed the lowest electrical resistance and polarization electrical resistance. Moreover, the passivation film of steel bars weakened with increasing distance from the surface of the steel bars. Therefore, the corrosion of steel bars becomes more serious with increasing distance. Finally, the influence of the rust inhibitor on the corrosion resistance of steel bars in the specimens decreased in the following order: 0.5% NaNO2 + 0.5% Benzotriazole >1.0% NaNO2>1.0% Benzotriazole.
Funding Information
  • National Natural Science Foundation of China (51808300, 51778302)
  • Natural Science Foundation of Ningbo Municipality (No. 2018A610357)

This publication has 40 references indexed in Scilit: