Electrical and Mechanical Characteristics of PbnBi4Tin+3O3n+12 Ceramics
Authors:
- Kazuo ShojiKSKazuo Shoji
- Tomoharu SakaiTSTomoharu Sakai
- Yasuo Uehara SakataYSYasuo Uehara Sakata
- 1 September 1997
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 36 (9S)
Abstract
The electrical and mechanical characteristics of Pb n Bi4Ti n +3O3 n +12 ceramics were examined. With increasing n, the dielectric constant ε s increased, and the temperature dependence of ε s broadened. ε s, at room temperature, reached a value of approximately 750 at n=3 and n=4 at 100 kHz. The dielectric breakdown strength E b and the three-point bending strength σ decreased with increasing n. For example, σ of the sample at n=4 was approximately a 70% value of the sample at n=0. On the other hand, the examination of the characteristics of grain-oriented samples clarified that E b and σ can be improved in the direction perpendicular to the polarization axis.Keywords
This publication has 3 references indexed in Scilit:
- Grain-Oriented Ceramics in Bismuth Layer-Structure Compounds for Capacitor MaterialJapanese Journal of Applied Physics, 1996
- Dielectric Breakdown Strength of Grain-Oriented Bi4Ti3O12 CeramicsJapanese Journal of Applied Physics, 1992
- Topotactical reactions with ferrimagnetic oxides having hexagonal crystal structures—IJournal of Inorganic and Nuclear Chemistry, 1959