Lately, materials research has shifted to composite materials from monolithic, adjusting to the global need for light weight, low cost, quality, and high performance in structural materials. Every effort aims to develop a material which can be appropriate for various industry and machinery purpose. In the present study, a modest attempt has been made to develop cast aluminum based silicon carbide (SiC) particulate metal matrix composite (MMC) and worked upon to raise the wettability factor between the matrix and dispersion phase. Magnesium (Mg) is used as wetting agent. It works by scavenging the oxygen from dispersoids surface and thinning the gas layer around dispersoids and this is done by forming MgO or MgAl 2 O 4 or both according to concentration of Magnesium added. Mg 2 Si is the compound responsible for strengthening. The combination of aluminum and magnesium seems to have synergetic effect on wetting and give appropriate strength. All mechanical properties obtained are well correlated with microstructure obtained by Scanning electron micrograph. Differential thermal analysis (DTA) and thermo gravimetric analysis (TGA) also justified the results obtained in present investigations.