Thermo-Mechanical Finite Element Analysis of Multi-Pass Finish Rolling of 70S-6 Welding Wire Steel: Effects of Pass Schedule, Finish Rolling Temperature, and Rolling Speed

Authors:
Open Access
Publisher website
Google Scholar
Abstract
With the advancement of welding technology, the demand for 70S-6 welding wire steel has steadily increased in industries such as construction, automotive, pressure vessels, and line pipe manufacturing. To optimize the production process of the target material, this study utilized the finite-element software ABAQUS to numerically simulate the multi-pass finish rolling process of 70S-6 welding wire steel. The study investigates the effects of the key rolling parameters—pass distribution (8/10/12 passes), finish rolling temperature (860/880/900 °C), and rolling speed (0.5 Vp/1.0 Vp/1.5 Vp, here Vp denotes the reference industrial rolling speed) on the rolling force, temperature field, and equivalent stress/strain during finish rolling. The results show that the increased number of passes homogenizes deformation, reduces local stress concentration and enhances mechanical properties. Specifically, 12 passes reduce the peak rolling force from 250,972 N to 208,124 N, significantly enhancing stress and temperature uniformity across the section. Increasing the finish rolling temperature lowers the pass-averaged flow stress and attenuates rolling-force fluctuations. At 880 °C, the simulated core–surface temperature gradient is minimal (50 °C), whereas at 900 °C the gradient increases (80 °C) but the rolling-force histories exhibit a lower peak level and smaller low-frequency oscillations; thus 880 °C is preferable when through-thickness thermal uniformity is targeted, while 900 °C is more suitable when a smoother load response is required. Increasing the finish rolling speed from 0.5 Vp to 1.5 Vp reduces the peak rolling force from 233,165 N to 183,665 N and significantly damps low-frequency load oscillations. However, it concurrently intensifies stress localization at the outer-surface tracking points P3/P4, which are in direct contact with the rolls, where the local equivalent stress approaches 523 MPa, even though the overall strain distribution along the bar length becomes more uniform. Overall, the optimal processing window is identified as a 12-pass schedule, a finish rolling temperature of 880–900 °C, and a rolling speed of 1.0–1.5 Vp, which can improve both rolling quality and temperature and stress and strain uniformity.

This publication has 44 references indexed in Scilit: