Elastic Fibre Prestressing Mechanics within a Polymeric Matrix Composite
Open Access
Abstract
The elastic fibre prestressing (EFP) technique has been developed to balance the thermal residual stress generated during curing of a polymeric composite. The continuous fibre reinforcements are prestressed and then impregnated into a polymeric matrix, where the prestress load is only removed after the resin is fully cured in order to produce an elastically prestressed polymeric matrix composite (EPPMC). Although the EFP is active in improving the static mechanical performance of a composite, its mechanics on dynamic mechanical performance and viscoelasticity of a composite is still limited. Here, we established a theoretical model in order to decouple the EFP principle, aiming to better analyse the underlying mechanics. A bespoke fibre prestressing rig was then developed to apply tension on a unidirectional carbon-fibre-reinforced epoxy prepreg to produce EPPMC samples with various EFP levels. The effects of EFP were then investigated by carrying out both static and dynamic mechanical testing, as well as the viscoelastic creep performance. It was found that there is an optimal level of EFP in order to maximise the prestress benefits, whilst the EFP is detrimental to the fibre/matrix interface. The EFP mechanisms are then proposed based on these observations to reveal the in-plane stress evolutions within a polymeric composite.Keywords
Funding Information
- National Natural Science Foundation of China (52005108, 52275096, 51675103, 2019I0004, MSV-2018-07, 18ZR1414200, GXRC-20066)
- Fuzhou-Xiamen-Quanzhou National Independent Innovation Demonstration Zone High-end Equipment Vibration and Noise Detection and Fault Diagnosis Collaborative Innovation Platform Project, Fujian Provincial Science and Technology Project (52005108, 52275096, 51675103, 2019I0004, MSV-2018-07, 18ZR1414200, GXRC-20066)
- State Key Laboratory of Mechanical Systems, and Vibration (52005108, 52275096, 51675103, 2019I0004, MSV-2018-07, 18ZR1414200, GXRC-20066)
- Shanghai Natural Sciences Fund (52005108, 52275096, 51675103, 2019I0004, MSV-2018-07, 18ZR1414200, GXRC-20066)
- Start-up Funding from Fuzhou University (52005108, 52275096, 51675103, 2019I0004, MSV-2018-07, 18ZR1414200, GXRC-20066)
This publication has 36 references indexed in Scilit:
- The use of carbon nanofibers for thermal residual stress reduction in carbon fiber/epoxy laminated compositesCarbon, 2013
- Bistable prestressed buckled laminatesComposites Science and Technology, 2008
- Force measurement from viscoelastically recovering Nylon 6,6 fibresMaterials Letters, 2008
- A New Method to Reduce Cure-Induced Stresses in Thermoset Polymer Composites, Part III: Correlating Stress History to Viscosity, Degree of Cure, and Cure ShrinkageJournal of Composite Materials, 2000
- Interpretation of fiber fragmentation in carbon/epoxy single fiber composites: Possible fiber pre‐tension effectsPolymer Engineering & Science, 1992
- Mechanical property and residual stress development during cure of a graphite/BMI compositePolymer Engineering & Science, 1990
- A Mechanical/Thermal Analysis of Prestressed Composite LaminatesJournal of Composite Materials, 1988
- Effect of heat treatment on the distribution of residual stresses and the properties of epoxy polymersMechanics of Composite Materials, 1987
- An Experimental Study of the Effect of Prestressed Loose Carbon Strands on Composite StrengthJournal of Composite Materials, 1983
- Calculations of the Room-Temperature Shapes of Unsymmetric LaminatestwoJournal of Composite Materials, 1981