Microstructure and Mechanical Properties of TiC/TiB Composite Ceramic Coatings In-Situ Synthesized by Ultrasonic Vibration-Assisted Laser Cladding

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Laser cladding coating has many advantages in surface modification, such as a small heat-affected zone, and good metallurgical bonding. However, some serious problems such as pores, and poor forming quality still exist in the coating. To suppress these problems, a novel process of ultrasonic vibration-assisted laser cladding process was adopted to in-situ synthesize TiC/TiB composite ceramic coating on the surface of titanium alloy. Results showed that the introduction of ultrasonic vibration effectively improved the surface topography of the coating, reduced the number of pores in the coating, refined the crystal grains of the coating, decreased the residual tensile stress in the coating, and increased the micro-hardness of the coating. The tribological properties of the coating were significantly improved by the ultrasonic vibration, the wear resistance of the coating fabricated with ultrasonic vibration at power of 400 W increased about 1.2 times compared with the coating fabricated without ultrasonic vibration, and the friction coefficient decreased by 50%.
Funding Information
  • National Natural Science Foundation of China (51775559)
  • Research Initiation Fund of Changzhou University (ZMF21020020)
  • Fundamental Research Funds for Central Universities of the Central South University (160171022)

This publication has 31 references indexed in Scilit: