When a Small Amount of Comonomer Is Enough: Tailoring the Critical Solution Temperature of LCST-Type Thermoresponsive Random Copolymers by PEG Methyl Ether Methacrylate with 1100 g/mol Molecular Weight

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Tuning the critical solution temperature (CST) of thermoresponsive polymers is essential to exploit their immense potential in various applications. In the present study, the effect of PEG-methyl ether methacrylate with a higher molecular weight of 1100 g/mol (mPEGMA1100) as a comonomer was investigated for its suitability for the CST adjustment of LCST-type polymers. Accordingly, a library of mPEGMA1100-based copolymers was established with varying compositions (XmPEGMA1100) using four main comonomers, namely di(ethylene glycol) ethyl ether acrylate, N-isopropyl acrylamide and methacrylamide, and mPEGMA300, with different CST values (cloud points, TCP, and clearing points, TCL, by turbidimetry). It was found that less than 20 mol% of the mPEGMA1100 in the copolymers is practically sufficient for tuning the CST in the entire measurable temperature range, i.e., up to 100 °C, regardless of the CST of the homopolymer of the main comonomer (CST0). Moreover, a predictive asymptotic model was developed based on the measured CST values, which strikingly revealed that the CSTs of mPEGMA1100-containing copolymers depend only on the two main parameters of these copolymers, XmPEGMA1100 and the CST of the homopolymer of the main comonomer (CST0), that is, CST = f(CST0, XmPEGMA1100). The revealed two-parameter relationship defines a surface in 3D plotting, and it is applicable to determine the CST of copolymers in advance for a given composition or to define the suitable composition for a required CST value. These unprecedented results on the dependence of CSTs on two major well-defined parameters enable to design a variety of novel macromolecular structures with tailored thermoresponsive properties.
Funding Information
  • National Research, Development and Innovation Office, Hungary (PD139162, K135946, TKP2021-EGA-31)

This publication has 69 references indexed in Scilit: