Mixed mode fracture toughness of R260Mn rail steel using Compact Tension Shear specimens
Authors:
- Sjoerd T. HengeveldSHSjoerd T. Hengeveld
- Davide LeonettiDLDavide Leonetti
- H.H. (Bert) SnijderHSH.H. (Bert) Snijder
- Johan MaljaarsJMJohan Maljaars
Open Access
- 15 July 2025
- journal article
- Published by Elsevier in Procedia Structural Integrity
- Vol. 68, 1216-1222
Abstract
No abstract availableFunding Information
- M2i Materials Innovation Institute
This publication has 18 references indexed in Scilit:
- Analysis of fatigue crack growth under mixed mode (I + II) loading conditions in rail steel using CTS specimenEngineering Failure Analysis, 2020
- Experimental and numerical investigation on fracture behavior of CTS specimen under I-II mixed mode loadingEuropean Journal of Mechanics - A/Solids, 2018
- Mixed mode II and III fatigue crack growth in a rail steelInternational Journal of Fatigue, 2018
- Mixed mode fatigue crack propagation in a railway wheel steelProcedia Structural Integrity, 2016
- Introduction to the damage tolerance behaviour of railway rails – a reviewEngineering Fracture Mechanics, 2009
- Fracture Mechanics Determinations of Allowable Crack Size in Railroad RailsJournal of Failure Analysis and Prevention, 2007
- Fracture mechanics in railway applications––an overviewEngineering Fracture Mechanics, 2005
- Application of a Mode II Fracture Specimen to Plastically Deforming Material1989
- A crack opening stress equation for fatigue crack growthInternational Journal of Fracture, 1984
- SOME THEORETICAL AND EXPERIMENTAL ASPECTS OF MIXED MODE FRACTURES1984