Sensitization and remediation effects on environmentally assisted cracking of Al-Mg naval alloys
Authors:
- M. SeifiMSM. Seifi
- I. GhamarianIGI. Ghamarian
- P. SamimiPSP. Samimi
- P.C. CollinsPCP.C. Collins
- N.J.H. HolroydNHN.J.H. Holroyd
- J.J. LewandowskiJLJ.J. Lewandowski
- 1 July 2018
- journal article
- review article
- Published by Elsevier in Corrosion Science
- Vol. 138, 219-241
Abstract
No abstract availableKeywords
Funding Information
- National Science Foundation (1624748, ONR-N00014-14-1-0593, ONR-N00014-11-1-0406)
- Iowa State University (1624748, ONR-N00014-14-1-0593, ONR-N00014-11-1-0406)
- Colorado School of Mines (1624748, ONR-N00014-14-1-0593, ONR-N00014-11-1-0406)
- Center for Advanced Non-Ferrous Structural Alloys (1624748, ONR-N00014-14-1-0593, ONR-N00014-11-1-0406)
- Office of Naval Research (1624748, ONR-N00014-14-1-0593, ONR-N00014-11-1-0406)
This publication has 69 references indexed in Scilit:
- Influence of alloyed Nd content on the corrosion of an Al–5Mg alloyCorrosion Science, 2013
- Electrochemical behaviour of the β-phase intermetallic (Mg2Al3) as a function of pH as relevant to corrosion of aluminium–magnesium alloysCorrosion Science, 2013
- A study of intergranular fracture in an aluminium alloy due to hydrogen embrittlementInternational Journal of Plasticity, 2012
- Effects of microstructure on hydrogen-induced cracking in aluminum alloysScripta Materialia, 2011
- Delamination of a sensitized commercial Al–Mg alloy during fatigue crack growthScripta Materialia, 2010
- Precipitation behavior of the ß phase in Al-5083Materials Science and Engineering: A, 2010
- Crystallographic fatigue crack initiation in nickel-based superalloy René 88DT at elevated temperatureActa Materialia, 2009
- Stress Corrosion Cracking of Al-Mg and Mg-Al AlloysCorrosion, 2004
- Damage due to hydrogen embrittlement and stress corrosion crackingEngineering Failure Analysis, 2000
- Hydrogen Solubility, Diffusion and Trapping in High Purity Aluminum and Selected Al-Base AlloysMaterials Science Forum, 2000