Well-Defined ZIF-Derived Fe–N Codoped Carbon Nanoframes as Efficient Oxygen Reduction Catalysts

Authors:
Publisher website
Google Scholar
Abstract
A series of ZIF-derived Fe–N codoped carbon materials with a well-defined morphology, high surface area, tunable sizes and porous nanoframe structure was successfully prepared by synthesizing Fe-doped ZIF-8 through the assembly of Zn2+ ions with 2-methylimidazole in the presence of iron(III) acetylacetonate, followed by pyrolysis at a high temperature and in an Ar atmosphere. The prepared optimum catalyst materials exhibited excellent activity for the oxygen reduction reaction (ORR) and outstanding durability in both acidic and alkaline solutions. We found that Fe doping during the ZIF-8 synthesis stage was crucial to achieve the materials’ well-defined morphology, tunable size, good particle dispersion, and high performance. XPS revealed that Fe doping greatly enhanced the fractions of graphitic-N and pyridinic-N and decreased the fraction of oxidized-N. We suggest that the porosity and high surface area of the nanoframe structure originated from the metal–organic frameworks, the high dispersion of Fe in the nanoframe, and the enhanced proportions of active N species, all of which were responsible for the materials’ significantly enhanced ORR performance.
Funding Information
  • Guangdong Provincial Department of Science and Technology (2014A010105041, 2015B010106012, 2016A010103028)
  • China Postdoctoral Science Foundation (2016M592492)
  • National Natural Science Foundation of China (21276098, 21476088, 51302091, U1301245)
  • Natural Science Foundation of Guangdong Province (2015A030312007)
  • Guangdong Province Commission of Education (2013CXZDA003)

This publication has 56 references indexed in Scilit: