The corrosion of carbon steel under delaminating repair coatings after long‐term marine splash zone exposure

Authors:
Publisher website
Google Scholar
Abstract
Organic repair coatings are applied to repair areas of previously coated low‐carbon steel samples, and the samples are exposed to the splash zone in an offshore environment (Helgoland, North Sea) for 57 months. The volume loss of the steel underneath the delaminated coating is estimated with a three‐dimensional optical stripe line projection. The samples show a small variation in the degree of delamination (22%) only. The steel volume loss values, in contrast, range between 164 × 109 and 320 × 109 µm³, which is a variation of 196%. The degree of delamination of the scribed coatings does not mirror the corrosion of the steel underneath the delaminated sections. The coating with the widest degree of delamination exhibits the lowest steel volume loss due to corrosion. A good scribe performance of a coating is, therefore, no guarantee for a low corrosion loss nor for a low local corrosion depth in the steels to be protected.