Microstructure evolution and mechanical properties of transient liquid phase (TLP) bonded joints of TiAl intermetallics
Authors:
- Tiesong LinTLTiesong Lin
- Haixin LiHLHaixin Li
- Peng HePHPeng He
- Hongmei WeiHWHongmei Wei
- Liang LiLLLiang Li
- Jicai FengJFJicai Feng
- 1 June 2013
- journal article
- research article
- Published by Elsevier in Intermetallics
- Vol. 37, 59-64
Abstract
No abstract availableKeywords
This publication has 20 references indexed in Scilit:
- Mechanical milling of Ti–Ni–Si filler metal for brazing TiAl intermetallicsIntermetallics, 2011
- Superplastic diffusion bonding of γ-TiAl-based alloyMaterials Science and Engineering: A, 2004
- Effects of copper insert layer on the properties of friction welded joints between TiAl and AISI 4140 structural steelIntermetallics, 2004
- Development of a TiAl turbocharger for passenger vehiclesMaterials Science and Engineering: A, 2002
- Effects of brazing filler on properties of brazed joints between TiAl and metallic materialsIntermetallics, 2001
- Diffusion bonding of γ-TiAl sheetsIntermetallics, 1999
- Infrared joining strength and interfacial microstructures of Ti–48Al–2Nb–2Cr intermetallics using Ti–15Cu–15Ni foilIntermetallics, 1999
- Application of cast gamma TiAl for automobilesIntermetallics, 1998
- Electron beam welding of a Ti–45Al–2Nb–2Mn+0.8 vol.% TiB2 XD alloyMaterials Science and Engineering: A, 1997
- Diffusion bonding of intermetallic Ti-47Al-2Cr-0.2Si sheet material and mechanical properties of joints at room temperature and elevated temperaturesIntermetallics, 1997