Relationship of Mineralogical Composition to Thermal Expansion, Spectral Reflectance, and Physico-Mechanical Aspects of Commercial Ornamental Granitic Rocks

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The aim of the present study is to link the thermal expansion, spectral reflectance, and physico-mechanical aspects of different types of commercial granitic rocks with their mineralogical and chemical composition. The granitic rock types were characterized using several analyses, including petrography, chemical, mineralogical, and thermo-gravimetrical analysis using XRF, XRD, and TG/DTG/DSC techniques. The rock types were subjected to several performance tests, such as tests of their thermal expansion, spectral reflectance, and physico-mechanical properties. The results revealed that quartz, albite, and potash feldspar with minor amounts of mica (biotite/muscovite/annite) are the main mineralogical constitutes, in addition to some alteration minerals, such as kaolinite, saussorite, and prehnite. The studied granitic rocks were classified as monzogranite/syenogranite of high K-calc-alkaline and peraluminous characters and are related to late- to post-collisional settings. The thermogravimetrical analysis revealed that the overall mass loss over the whole temperature range up to 978 °C did not exceed 3% of the initial weight for all studied rocks. The results of thermal expansion revealed that the maximum change in linear thermal expansion for all rock types did not exceed 0.015% of their initial lengths at an unusual air temperature of 50 °C. The spectral analysis revealed that iron and hydroxyl ions are the main spectral absorption features that appeared in the VIS-NIR and SWIR regions, in addition to the appearance of the common and distinctive absorption peaks of the main mineral composition. Furthermore, the spectral reflectance demonstrated that the granitic rock types of low iron oxide content achieved a high reflectivity percent in the VIS-NIR and SWIR spectral regions compared with those of high iron content. As a general trend, the granitic rock types of high iron content and/or lower quartz content exhibited a high performance regarding their physical and mechanical properties, such as water absorption, apparent porosity, bulk density, compressive strength, and abrasion resistance. The results of water absorption, density, strength, and abrasion resistance of the studied granitic rocks are in the range of 0.14–0.31%, 2582–2644 kg/m3, 77.85–222.75 MPa, and 26.27–55.91 Ha, respectively, conforming to the requirements of ornamental stones according to the ASTM standard.

This publication has 30 references indexed in Scilit: