Effect of Injection Molding Conditions on Crystalline Structure and Electrical Resistivity of PP/MWCNT Nanocomposites
Open Access
Abstract
Polypropylene (PP) / multi-walled carbon nanotube (MWCNT) nanocomposites were prepared by melt-mixing and used to manufacture samples by injection molding. The effect of processing conditions on the crystallinity and electrical resistivity was studied. Accordingly, samples were produced varying the mold temperature and injection rate, and the DC electrical resistivity was measured. The morphology of MWCNT clusters was studied by optical and electron microscopy, while X-ray diffraction was used to study the role of the crystalline structure of PP. As a result, an anisotropic electrical behavior induced by the process was observed, which is further influenced by the injection molding processing condition. It was demonstrated that a reduction of electrical resistivity can be obtained by increasing mold temperature and injection rate, which was associated to the formation of the γ-phase and the related inter-cluster morphology of the MWCNT conductive network.Keywords
This publication has 53 references indexed in Scilit:
- Electrical properties and applications of carbon based nanocomposite materials: An overviewSurface and Coatings Technology, 2011
- Carbon nanofibers for strain and impact damage sensing in glass fiber reinforced composites based on an unsaturated polyester resinPolymer Composites, 2011
- Development of unsaturated polyester matrix – carbon nanofibers nanocomposites with improved electrical propertiesJournal of Applied Polymer Science, 2010
- A Route for Polymer Nanocomposites with Engineered Electrical Conductivity and Percolation ThresholdMaterials, 2010
- Dielectric properties and conductivity of carbon nanofiber/semi-crystalline polymer compositesActa Materialia, 2008
- Skin-Core Micro-Structure and Surface Orientation of Carbon Nanotube Composites by Injection Molding ProcessSolid State Phenomena, 2008
- Description and modeling of fiber orientation in injection molding of fiber reinforced thermoplasticsPolymer, 2005
- The γ-phase of high molecular weight isotactic polypropylene: III. The equilibrium melting point and the phase diagramPolymer, 1998
- Structure and properties of nucleated random and block copolymers of propyleneAdvances in Polymer Technology, 1994
- A.c. conduction in amorphous chalcogenide and pnictide semiconductorsAdvances in Physics, 1987