Self-diffusion in polycrystalline Li1+xTi2−xAlx(PO4)3 (0.2 ≤ x ≤ 0.4) samples followed by 7Li PFG (pulse field gradient) NMR spectroscopy

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Short and long range lithium motions in powder Li1+xTi2−xAlx(PO4)3 (LTAP) NASICON compounds prepared by ceramic (x = 0.2 and 0.4) and sol–gel (x = 0.3 and 0.4) routes are discussed. ND diffraction and MAS-NMR spectroscopy were previously used to investigate structural features of these compounds. In particular, Fourier map differences showed that the amount of Li atoms allocated at M3 increases at the expense of M1 sites when the Li content increases. In this work, PFG-NMR results show that diffusion coefficients rise with the amount of lithium and temperature. The restricted diffusion inside NASICON particles is compared with “free” diffusion processes. At 300 K, diffusion coefficients DPFG ∼ 5 × 10−12 m2 s−1 have been deduced in ceramic x = 0.2 and 0.4 samples, decreasing with diffusion time Δ used in PFG experiments. In sol–gel samples, diffusion coefficients are near those of ceramic samples, but decrease faster with diffusion Δ times, as a consequence of the Li confinement inside sub-micrometric crystallites. The NMR spin-echo signal displays minima at specific q(γgδ) values that are related to the crystallite size. From Rdif ∼ qm −1 distances, calculated from the position of minima, and from diffusion coefficients deduced for high Δ values, the mean crystallite size was estimated. Finally, from the temperature dependence of conductivity and diffusion coefficients, the activation energy and charge carriers concentrations were determined.
Funding Information
  • Ministerio de Asuntos Económicos y Transformación Digital, Gobierno de España (MAT2016-78362-C4-2R, PID2019-106662RB-C42)
  • Agencia Estatal de Investigación (M-Era-Net 2016/PCIN-110-2017)

This publication has 44 references indexed in Scilit: