EBSD investigation of the microstructure and texture characteristics of hot deformed duplex stainless steel
- 1 May 2006
- journal article
- Published by Wiley in Journal of Microscopy
- Vol. 222 (2) , 85-96
Abstract
Summary: The microstructure and crystallographic texture characteristics were studied in a 22Cr‐6Ni‐3Mo duplex stainless steel subjected to plastic deformation in torsion at a temperature of 1000 °C using a strain rate of 1 s−1. High‐resolution EBSD was successfully used for precise phase and substructural characterization of this steel. The austenite/ferrite ratio and phase morphology as well as the crystallographic texture, subgrain size, misorientation angles and misorientation gradients corresponding to each phase were determined over large sample areas. The deformation mechanisms in each phase and the interrelationship between the two are discussed.Keywords
This publication has 20 references indexed in Scilit:
- EBSD study of the orientation dependence of substructure characteristics in a model Fe−30wt%Ni alloy subjected to hot deformationJournal of Microscopy, 2005
- EBSD and TEM investigation of the hot deformation substructure characteristics of a type 316L austenitic stainless steelJournal of Microscopy, 2004
- A model of continuous dynamic recrystallizationActa Materialia, 2003
- Flow stress and ductility of duplex stainless steel during high-temperature torsion deformationMetallurgical and Materials Transactions A, 2002
- Influence of microstructure on the flow behavior of duplex stainless steels at high temperaturesMetallurgical and Materials Transactions A, 2000
- An experimental study of the recrystallization mechanism during hot deformation of aluminiumMaterials Science and Engineering: A, 2000
- A mechanism of ferrite softening in a duplex stainless steel deformed in hot torsionMaterials Science and Engineering: A, 1997
- Texture development during the torsion testing of α-iron and two IF steelsActa Materialia, 1996
- Microstructure and local crystallographic evolution in an Al1 wt% Mg alloy deformed at intermediate temperature and high strain-rateActa Materialia, 1996
- Overview no. 96 evolution of f.c.c. deformation structures in polyslipActa Metallurgica et Materialia, 1992