Evolution of Microstructure and Mechanical Properties of Titanium Grade 4 with the Increase of the ECAP-Conform Passes

Authors:
Publisher website
Google Scholar
Abstract
This work reports on the results of investigation of microstructure change of commercially pure titanium Grade 4 with the increase of the number of ECAP-Conform passes. There has been investigated influence of continuous equal-channel angular pressing by the scheme “Conform” (ECAP-C) on the structure and properties of commercially pure titanium Grade 4. It has been demonstrated that as a result of first two ECAP-C cycles titanium structure is strongly fragmented and deformation bands are formed. With the further increase of ECAP-C passes to 6 the band structure is transformed into ultrafine-grained (UFG) structure with the grain size of about 250 nm. The strength of titanium regularly grows with the increase of the number of ECAP-C passes, while ductility, which settles after first cycle on the level of 12%, is almost not changed with the further strain degree increase. As a result of the subsequent drawing of titanium after ECAP-C its strength additionally increases to 1300 MPa, with retention of ductility about 11%.