Visualizing Interfacial Energy Offset and Defects in Efficient 2D/3D Heterojunction Perovskite Solar Cells and Modules

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Currently, the full potential of perovskite solar cells (PSCs) is limited by chargecarrier recombination owing to imperfect passivation methods. Here, the recombination loss mechanisms owing to the interfacial energy offset and defects are quantified. The results show that a favorable energy offset can reduce minority carriers and suppress interfacial recombination losses more effectively than chemical passivation. To obtain high‐efficiency PSCs, 2D perovskites are promising candidates, which offer powerful field effects and require only modest chemical passivation at the interface. The enhanced passivation and charge‐carrier extraction offered by the 2D/3D heterojunction PSCs has boosted their power conversion efficiency to 25.32% (certified 25.04%) for small‐size devices and to 21.48% for a large‐area module (with a designated area of 29.0 cm2). Ion migration is also suppressed by the 2D/3D heterojunction, such that the unencapsulated small‐size devices maintain 90% of their initial efficiency after 2000 h of continuous operation at the maximum power point.
Funding Information
  • National Key Research and Development Program of China (2018YFB1500103)
  • National Natural Science Foundation of China (62004199)

This publication has 37 references indexed in Scilit: