Data analysis of striation spacing, lifetime, and crack length in crankshaft ductile cast iron under cyclic bending loading through high-cycle fatigue regime
Open Access
- 12 October 2022
- journal article
- research article
- Published by Elsevier in Data in Brief
- Vol. 45, 108666
Abstract
No abstract availableKeywords
Funding Information
- Ministry of Science Research and Technology (16-99-02-000087)
This publication has 24 references indexed in Scilit:
- Ductile cast irons: Microstructure influence on the damaging micromechanisms in overloaded fatigue cracksEngineering Failure Analysis, 2017
- Fatigue and Fracture Resistance of Heavy-Section Ferritic Ductile Cast IronMetals, 2017
- Comparison of Fatigue Properties of Nodular Cast Iron at Low and High Frequency Cyclic LoadingProcedia Engineering, 2017
- Crankshaft failure analysis of a boxer diesel motorEngineering Failure Analysis, 2015
- Fracture toughness and growth of short and long fatigue cracks in ductile cast iron EN‐GJS‐400‐18‐LTFatigue & Fracture of Engineering Materials & Structures, 2011
- A model for the formation of fatigue striations and its relationship with small fatigue crack growth in an aluminum alloyInternational Journal of Fatigue, 2010
- Fatigue crack propagation damaging micromechanisms in ductile cast ironsEngineering Fracture Mechanics, 2008
- Failure analysis of a crankshaft made from ductile cast ironEngineering Failure Analysis, 2006
- Crack propagation life prediction for Ti-6Al-4V based on striation spacing measurementsInternational Journal of Fatigue, 2000
- Prediction of fatigue crack propagation life in notched members under variable amplitude loadingJournal of Materials Engineering and Performance, 1997