Effect of Calcination Temperature on Mechanical Properties of Magnesium Oxychloride Cement

Authors:
Open Access
Publisher website
Google Scholar
Abstract
In order to make full use of magnesium chloride resources, the development and utilisation of magnesium oxychloride cement have become an ecological and economic goal. Thus far, however, investigations into the effects on these cements of high temperatures are lacking. Herein, magnesium oxychloride cement was calcinated at various temperatures and the effects of calcination temperature on microstructure, phase composition, flexural strength, and compressive strength were studied by scanning electron microscopy, X-ray diffraction, and compression testing. The mechanical properties varied strongly with calcination temperature. Before calcination, magnesium oxychloride cement has a needle-like micromorphology and includes Mg(OH)2 gel and a trace amount of gel water as well as 5 Mg(OH)2·MgCl2·8H2O, which together provide its mechanical properties (flexural strength, 18.4 MPa; compressive strength, and 113.3 MPa). After calcination at 100 °C, the gel water is volatilised and the flexural strength is decreased by 57.07% but there is no significant change in the compressive strength. Calcination at 400 °C results in the magnesium oxychloride cement becoming fibrous and mainly consisting of Mg(OH)2 gel, which helps to maintain its high compressive strength (65.7 MPa). When the calcination temperature is 450 °C, the microstructure becomes powdery, the cement is mainly composed of MgO, and the flexural and compressive strengths are completely lost.

This publication has 20 references indexed in Scilit: