Effects of irradiation on interfacial strength and microstructure of double-layer mullite and alumina coating on SiC
Authors:
- Taichi MiyagishiTMTaichi Miyagishi
- Sosuke KondoSosuke Kondo
- Hirokazu KatsuiHKHirokazu Katsui
- Kiyohiro YabuuchiKiyohiro Yabuuchi
- Ryutaro UsukawaRURyutaro Usukawa
- Yasuyuki OginoYOYasuyuki Ogino
- Hao YuHYHao Yu
- Ryuta KasadaRyuta Kasada
Open Access
- 15 September 2024
- journal article
- research article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 603
Abstract
No abstract availableKeywords
Funding Information
- Tohoku University
- Tohoku University
- Monbu Kagakusho
This publication has 32 references indexed in Scilit:
- Evaluation of the strength of FeCrAl alloy/surface Oxide film interface by micro double-notch shear testFusion Engineering and Design, 2024
- Microstructure and integrity of multilayer ceramic coating with alumina top coat on silicon carbide by laser chemical vapor depositionCeramics International, 2022
- Compressive strength degradation of SiC fibers exposed to high temperatures due to impurity-induced internal oxidationJournal of the European Ceramic Society, 2022
- Progress in development of SiC-based joints resistant to neutron irradiationJournal of the European Ceramic Society, 2020
- Corrosion behavior of ion-irradiated SiC in FLiNaK molten saltCorrosion Science, 2020
- High-dose, intermediate-temperature neutron irradiation effects on silicon carbide composites with varied fiber/matrix interfacesJournal of the European Ceramic Society, 2019
- Dissolution corrosion of 4H‐SiC in lead‐bismuth eutectic at 550°CMaterials and Corrosion, 2019
- Radiation-tolerant joining technologies for silicon carbide ceramics and compositesJournal of Nuclear Materials, 2014
- Densification and thermal gradient evolution of alumina during microwave sintering at 2.45GHzCeramics International, 2013
- Mullite2005