Evidence for carrier compensation by gallium vacancies during annealing of highly Si-doped β-Ga2O3
Authors:
- Katie R. GannKGKatie R. Gann
- Naomi A. PieczulewskiNPNaomi A. Pieczulewski
- Cameron A. GorsakCGCameron A. Gorsak
- Joshua T. BuontempoJBJoshua T. Buontempo
- Brenton A. NoesgesBNBrenton A. Noesges
- Thaddeus AselTAThaddeus Asel
- Daniel M. DrydenDDDaniel M. Dryden
- Hari P. NairHNHari P. Nair
- David A. MuellerDMDavid A. Mueller
- Michael O. ThompsonMTMichael O. Thompson
Open Access
- 16 September 2025
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 138 (11)
Abstract
Net carrier densities in highly Si-doped β-Ga2O3 decrease during thermal annealing as a function of temperature, time, and PO2 for both in situ and implant-doped films. The mechanism for this loss has been attributed to the formation of gallium vacancies (VGa3−), which act as compensating acceptors and form passivating defect complexes. Samples doped above 3 × 1019 cm−3, annealed at the same temperature and PO2, ultimately approach a similar net carrier density of 1–3 × 1019 cm−3 (for 950 °C and PO2 < 2 × 10−7 bar) independent of the starting dopant concentration or doping method. These highly doped samples, metastable under these conditions, generate VGa3− to reach the steady state |ND − NA|, determined by the Fermi level. An activation energy of 1.6 ± 0.2 eV was observed for the rate of net carrier loss in high concentration in situ doped films. Scanning transmission electron microscopy and electrical results for implanted samples show that dopant activation, lattice recovery, and compensation are all active within the first minutes of annealing. Understanding the metastability of higher doping levels and VGa3− formation allows for the development of mitigation strategies to achieve highly Si-doped β-Ga2O3 by implant (8 × 1019 cm−3 with >70 cm2/V s mobility), including using the minimum required anneal time to achieve lattice recovery and dopant activation, reducing vacancy formation. Compensation initially limited full activation of deeper implants to 1 × 1020 cm−3; by protecting the free surface with a SiO2 cap during annealing, the activation efficiency doubled, and the mobility increased by 30%, highlighting the importance of controlling VGa3− formation and compensation.Keywords
Funding Information
- Air Force Research Laboratory (FA9550-18-1-0529)
- Cornell Center for Materials Research (DMR-1719875)
- National Science Foundation (NNCI-2025233)
This publication has 41 references indexed in Scilit:
- Silicon Ion Implant Activation in β-(Al0.2Ga0.8)2O3Journal of Electronic Materials, 2024
- Universal radiation tolerant semiconductorNature Communications, 2023
- Projected Cost of Gallium Oxide Wafers from Edge-Defined Film-Fed Crystal GrowthCrystal Growth & Design, 2022
- Investigation of p-type doping in β- and κ-Ga2O3Journal of Alloys and Compounds, 2021
- On the bulk β-Ga2O3 single crystals grown by the Czochralski methodJournal of Crystal Growth, 2014
- Oxygen vacancies and donor impurities in β-Ga2O3Applied Physics Letters, 2010
- SRIM – The stopping and range of ions in matter (2010)Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 2010
- Gallium oxide thin films: A new material for high-temperature oxygen sensorsSensors and Actuators B: Chemical, 1991
- Some electrical properties of the semiconductor βGa2O3Journal of Physics and Chemistry of Solids, 1967
- Polymorphism of Ga2O3 and the System Ga2O3—H2OJournal of the American Chemical Society, 1952