Nacre‐Mimetic Nanocomposite Aerogels with Exceptional Mechanical Performance for Thermal Superinsulation at Extreme Conditions

Authors:
Top Cited Papers
Publisher website
Google Scholar
Abstract
Thermal protection under extreme conditions requires materials with excellent thermal insulation properties and exceptional mechanical properties to withstand a variety of complex external stresses. Mesoporous silica aerogels are the most widely used insulation materials due to their ultralow thermal conductivity. However, they still suffer from mechanical fragility and structural instability in practical applications. Herein, a nacre‐mimetic nanocomposite aerogel, synthesized via in situ growth of inorganic minerals in a lamellar cellulose nanofibrous network, is reported. The multiscale structural adaptation of the inorganic–organic components endows nanocomposite aerogels with rapid configuration recovery during ambient pressure drying. The resulting aerogels show ultralow thermal conductivities (17.4 mW m−1 K−1 at 1.0 atm). These aerogels also integrate challenging mechanical properties, including high compressive stiffness to resist deformation under the pressure of an adult, superelasticity to prevent static and dynamic stress cracking even under the crushing of a vehicle (1.6 t), and high bending flexibility to adapt to any surface. Moreover, they exhibit excellent structural stability under fatigue stress/strain cycles over a wide temperature range (−196 to 200 °C). The combination of high thermal insulation performance and excellent mechanical properties offers a potential material system for robust thermal superinsulation under extreme conditions, especially for aerospace applications.
Funding Information
  • National Key Research and Development Program of China (2021YFB3701603)
  • National Natural Science Foundation of China (52103075, 51973030, 52273031)
  • Science and Technology Commission of Shanghai Municipality (20JC1414900)
  • China Postdoctoral Science Foundation (2022M710664, 2022T150111)
  • National University of Defense Technology

This publication has 62 references indexed in Scilit: