Multiple Hydrogen Bonding-Assisted High-Strength Hydrogel of Silica/Polyacrylamide Nanocomposite Cross-Linked with Polyethylenimine

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The nanocomposite gel system has been successfully applied as a water shutoff agent to enhance oil recovery (EOR) or for plugging to control lost circulation events. In this study, the silica/polyacrylamide nanocomposite was synthesized via in situ free radical polymerization of acrylamide (AM) monomers in the presence of silica nanoparticles. The composite was cross-linked with polyethylenimine to prepare a high-strength hydrogel. The viscosity test was conducted to determine the gelation time of the gel. Rheological measurements and sand pack breakthrough pressure tests were carried out to measure the gel strength. Attenuated total reflectance-Fourier transform infrared (ATR-FTIR) and scanning electron microscopy (SEM) tests were adopted to characterize the structure and morphology of the gel. The results show that compared to polyacrylamide (PAM) gel, the gelation time of the nanocomposite gel will decrease with increasing gel elasticity modulus, and the breakthrough pressure of the nanocomposite gel is 29.82 MPa, which increased by 65%. As shown in the ATR-FTIR test, this can be attributed to the presence of multiple hydrogen bonds for the PAM molecule with both silica and quartz sand particles. In the composite gel, hydrogen bonding mainly forms between the O atoms of PAM and the H atom on the surface of silica, enhancing gel strength and elasticity modulus with more cross-linking density and less porosity. Moreover, H bonding between additional -NH2 of PAM and quartz sand particles helps improve gel plugging pressure. However, in the silica and PAM mixture gel, the H bonding of silica occupies -NH2 of PAM, which became unavailable to attach on the sand surface, reducing the breakthrough pressure by 30%, although it can enhance the rheological strength. This study suggests that in situ composite of silica in PAM can not only greatly improve gel rheological strength but also help maintain the strong adhesion of PAM molecules onto quartz sand, resulting in better plugging performance in the sand reservoir.
Funding Information
  • Natural Science Foundation of Jiangsu Province (BK20190930)
  • Basic Research Program of Jiangsu Education Department (19KJB440003)
  • National Natural Science Foundation of China (52004037, 52074329, 52288101)

This publication has 27 references indexed in Scilit: