Experimental and computational study of damage behavior of tungsten under high energy electron beam irradiation
Authors:
- Muyuan LiMLMuyuan Li
- Mathias SommererMSMathias Sommerer
- Ewald WernerEWEwald Werner
- Stefan LampenscherfSLStefan Lampenscherf
- Thorsten SteinkopffTSThorsten Steinkopff
- Philipp WolfrumPWPhilipp Wolfrum
- 1 February 2015
- journal article
- research article
- Published by Elsevier in Engineering Fracture Mechanics
- Vol. 135, 64-80
Abstract
No abstract availableKeywords
This publication has 13 references indexed in Scilit:
- Fracture mechanical analysis of tungsten armor failure of a water-cooled divertor targetFusion Engineering and Design, 2014
- Comparison of the thermal shock performance of different tungsten grades and the influence of microstructure on the damage behaviourPhysica Scripta, 2011
- Loading rate dependence of the fracture toughness of polycrystalline tungstenJournal of Nuclear Materials, 2011
- Thermal shock characterization of tungsten deformed in two orthogonal directionsJournal of Nuclear Materials, 2011
- Performance of different tungsten grades under transient thermal loadsNuclear Fusion, 2011
- Fracture toughness of polycrystalline tungsten alloysInternational Journal of Refractory Metals and Hard Materials, 2010
- Cracking failure study of ITER-reference tungsten grade under single pulse thermal shock loads at elevated temperaturesJournal of Nuclear Materials, 2009
- Probabilistic failure analysis of a water-cooled tungsten divertor: Impact of embrittlementJournal of Nuclear Materials, 2008
- EU Development of High Heat Flux ComponentsFusion Science and Technology, 2005
- Analysis of singular interface stresses in dissimilar material joints for plasma facing componentsJournal of Nuclear Materials, 2001