Influence of crack propagation direction on {110} fracture toughness of gallium arsenide

Authors:
Publisher website
Google Scholar
Abstract
Cleavage of {110} planes in a GaAs single crystal was investigated to study whether propagation direction influences the measured fracture toughness. The propagation direction for cracks on the (110) plane was varied to be [001], [112], [111], [110] and [001]. Pre-cracks were introduced by Vickers hardness indents, and through-thickness-pre-crack bend bars were also tested. One orientation, (110)[110], tested only with the latter method, had a substantially lower toughness than the others, suggesting the existence of one specific ‘easy’ propagation direction. Possible reasons for toughness differences with respect to the propagation direction are discussed. Different testing methods to resolve such issues as firstly direct determination of fracture toughness from indenter cracks, secondly bending fracture toughness experiments from indenter pre- cracks, and thirdly bending fracture toughness experiments from through- thickness pre-cracks are critically compared for their potential to resolve toughness anisotropies.

This publication has 16 references indexed in Scilit: