Compactibility and Fibre Volume Fraction Limits of Unidirectional Discontinuous Carbon Fibre Thermoset Prepreg Laminates
Open Access
Abstract
The aim of this study was to explore the compactibility of unidirectional staple carbon fibre laminates in comparison with their uni- and biaxial continuous fibre counterparts. Resin-preimpregnated plies were inserted into a heated compression mould at an elevated mould temperature of 110 °C. By applying stepwise loading, the correlation between consolidation pressure and fibre volume content was derived and related to fibre orientation distribution. The fibre orientation distribution is obtained from photographic image analyses of 2D ply sections of the same samples using the structure tensor approach. For commonly used autoclave prepreg pressure of 6.8 bar results indicate that lower-oriented staple carbon fibre unidirectional laminates with a fibre orientation distribution factor η0 = 0.74 can potentially reach a maximum of 39% fibre volume fraction, while higher-oriented laminates with η0 = 0.78 end up at 43%. An exponential extrapolation suggests that a consolidation pressure of ≥90 bar is required to achieve 60% fibre volume content with highly oriented unidirectional staple carbon fibre laminates.Keywords
This publication has 41 references indexed in Scilit:
- Engineering interfacial thermal transport through comparative analysis of electrospraying and dip coating of silanized h-BN for thermo-mechanical enhancement of CF/Epoxy compositesComposites Part A: Applied Science and Manufacturing, 2025
- Fiber identification of braided composites using micro-computed tomographyComposites Communications, 2021
- Methodology of dry and wet compressibility measurementComposites Part A: Applied Science and Manufacturing, 2020
- Characterization and elastic property modeling of discontinuous carbon fiber reinforced thermoplastics prepared by a carding and stretching system using treated carbon fibersComposites Part A: Applied Science and Manufacturing, 2019
- A novel manufacturing method for aligned discontinuous fibre composites (High Performance-Discontinuous Fibre method)Composites Part A: Applied Science and Manufacturing, 2014
- Characterization of carbon fibers using X-ray phase nanotomographyCarbon, 2014
- Characterizing the Collagen Fiber Orientation in Pericardial Leaflets Under Mechanical Loading ConditionsAnnals of Biomedical Engineering, 2012
- Correlation between sizing formulation and compressive behavior of concentrated glass bundle suspensionsPolymer Composites, 2005
- The packing stress of impregnated fiber matsPolymer Composites, 2001
- A structure and property based process window for void free thermoset compositesPolymer Composites, 2001